PAINT FIRE-RETARDANT DISTENDING ITSELF “[UNIPOL] " ® stamp OV TU 2316-004-59846005-2007 The paint “OF [UNIPOL]” ® stamp OV is tested down the fire-retardant effectiveness before the specialized organization, which has the appropriate accreditation, with the formulation of the certificate of fire safety. Fire-retardant effectiveness of 1,5 hours. Paint is the distending itself closegrained fire-retardant system for the carrying steel constructions. Surface preparation The surface of the metal structures before the application of coating must be preliminary purified of mud, rust, slag, water-soluble salts and old paint. Fatty pollution beyond the surface it is necessary to remove by organic solvents or by the washing compositions throughout the beginning of mechanical cleaning in accordance with ALL-UNION STATE STAN. 9.402. After cleaning of metal structures the surface must be protected by ground [GF]-021 with a thickness of up to 0,05 mm. Method of application Before the application fire-retardant paint must be thoroughly mixed throughout entire volume during 5 minutes in a mechanized manner or during 15 minutes by hand, maintained before the putting around the disappearance of bubbles not less than 10 minutes. For the best of the hiding power of surface and achievement of the necessary (working) viscosity it is necessary to add the diluent before the direct application of material before a quantity to 10% of the total volume of paint before the capacity. Sediment on the bottom of container is not allowed. Diluent - water. For the washing of tool, container and spots so it is possible to use water. Work on fire protection of metal structures is conducted before the following order: paint down the surface is brought in layers by airless dispersion either by pneumatic spraying, by painter's brush or by roller. Each freshly applied layer must be dried and that following is brought after drying of previous down degree of 3. With a change in the ambient temperature the time of drying can increase or be reduced. Putting conditions The temperature of ambient air during putting of paint beyond the surface, which is subject down protection must be not lower than 5o[S], the relative humidity of air to 80%. The application of coating beyond the steel columns of the double-T profile cross section of № 20 (given thickness of [metalla]3,4 mm) for the sake of the thickness not of less than 1,0 mm ensures fire-retardant effectiveness not less than 0,75 hours (4-[aya] group of fire-retardant effectiveness). The application of coating beyond the steel columns of the double-T profile cross section of №30 and №60 (given thickness of metal 4,13 mm and 7,42 mm respectively) with the thickness is not less than 2,45 mm and 1,6 mm respectively ensure fire-retardant effectiveness not less than 1,5 hours. The thickness of coating is measured with the aid of the thickness gauge of the type Of minitest 2100 or by similar with an error of measurement not more than 2%. Expenditure, the thickness of the coating The expenditure of paint during putting of one layer composes 400-600 [g]/[m]2. For obtaining the layer of coating 2,45[mm] it is necessary to apply not less than 4-5- TI of layers, the expenditure of fire-retardant paint will compose [rpi] this of 3,4 [kg]/[m]2. For obtaining the layer of coating 1,60 mm it is necessary to apply not less 3rd layers. For obtaining the layer of coating 1,0 mm it is necessary to apply not less 2nd layers. Precautionary measures It is ecologically safe, nontoxic, fire-and-explosion-proof, the application of a paint is possible in the closed and badly aired accomodations. Transportation, storage, the guarantee Paint is transported at a temperature higher than 5o[S]. Composition to store before the tightly closed container at a temperature higher than 5o[S], protecting from the action of heat and straight solar rays. Guarantee period of storage - 12 months based on the day of production before the hermetically sealed container of manufacturing plant. Technical specifications № in sequence Designation of the index Norma 1. Color of the coating about the agreement 2. The exterior view of the paint The viscous fluid 3. The exterior view of the coating Surface must be flat, not have cracks, scalings, inflations. 4. A mass fraction of non-volatile substances, %, is not less 70 5. The coefficient of distention at a temperature of 800o[S], is more 20 6. The fire-retardant effectiveness of coating for the steel constructions, is not less 90 minutes 7. The time of drying the coating with a thickness of 400 m down the degree “of 3” at a temperature of 20o[S] and relative humidity of air (65±5)%, hour, is not more 1