PAINT FIRE-RETARDANT DISTENDING ITSELF “[UNIPOL] " ® stamp OP TU 2316-005-59846005-2007 The paint “OF [UNIPOL]” ® stamp OP is tested down the fire-retardant effectiveness before the specialized organization, which has the appropriate accreditation, with the formulation of the certificate of fire safety. Limit of the fire resistance of 1,5 hours. Paint is the distending itself closegrained fire-retardant system for the carrying steel constructions. Surface preparation The surface of the metal structures before the application of coating must be preliminary purified of mud, rust, slag, water-soluble salts and old paint. Fatty pollution beyond the surface it is necessary to remove by organic solvents or by the washing compositions throughout the beginning of mechanical cleaning in accordance with ALL-UNION STATE STAN. 9.402. After cleaning of metal structures the surface must be protected by ground [GF]-021 with a thickness of up to 0,05 mm. Method of application Before the application fire-retardant paint must be thoroughly mixed throughout entire volume during 5 minutes in a mechanized manner or during 15 minutes by hand, maintained before the putting around the disappearance of bubbles not less than 10 minutes. For the best of the hiding power of surface and achievement of the necessary (working) viscosity it is necessary to add the solvent before the direct application of material before a quantity to 10% of the total volume. Sediment on the bottom of container is not allowed. Diluents: toluene, xylene, solvent. The same solvents can be used for the washing of tool, container and spots. Work on fire protection of metal structures is conducted before the following order: paint down the surface is brought in layers by airless dispersion either by pneumatic spraying, by painter's brush or by roller. Each freshly applied layer must be dried and that following is brought after drying of previous down degree of 3. With a change in the ambient temperature the time of drying can increase or be reduced. Putting conditions Temperature of ambient air during putting of paint beyond the surface, which is subject down protection, from minus of 25o[S] to plus of 35o[S], the relative humidity of air to 80%. The application of coating beyond the steel columns of the double-T profile cross section of №30 and №60 (given thickness of metal 4,13 mm, 5,8 mm and 7,42 mm respectively) with the thickness is not less than 2,45 mm, 1,95 mm and 1,6 mm ensure fire-retardant effectiveness not less than 1,5 hours. The thickness of coating is measured with the aid of the thickness gauge of the type Of minitest 2100 or by similar with an error of measurement not more than 2%. Expenditure, the thickness of the coating Given thickness of metal, mm Thickness of coating, mm The theoretical flow rate of paint, [kg]/[m]2 7,42 1,65 2,6 5,8 1,95 2,9 4,1 2,45 3,65 The expenditure of paint during putting of one layer composes 400-600 [g]/[m]2. For obtaining the layer of coating 2,45 mm it is necessary to apply not less than 4-5- TI of layers. For obtaining the layer of coating 1,95 mm it is necessary to apply not less 4th layers. For obtaining the layer of coating 1,65 mm it is necessary to apply not less 3rd layers. Precautionary measures With conducting of internal work, and after their end thoroughly to also air accomodation. To use individual protective means. Storage, the guarantee Not to heat. To take care from the fire. Composition to store before the solidly closed container, protecting from the action of heat and straight solar rays. Guarantee period of storage - 12 months based on the day of production before the hermetically sealed container of manufacturing plant. Technical specifications № in sequence Designation of the index Norma 1. Color of the coating Any about the agreement for the sake of the customer or on catalog RAL 2. The exterior view of the paint The viscous fluid of any color 3. The exterior view of the coating Surface must be flat, not have cracks, scalings, inflations. 4. A mass fraction of non-volatile substances, %, is not less 70 5. The coefficient of distention at a temperature of 800o[S], is more 20 6. The fire-retardant effectiveness of coating for the steel constructions, is not less 90 minutes 7. The time of drying the coating with a thickness of 400 m down the degree “of 3” at a temperature of 20o[S] and relative humidity of air (65±5)%, hour, is not more 1 Time of drying the coating with a thickness of 300-350 m down degree of 1 and 3 depending on the temperature: Temperature of air, deg. [s] Time of drying down degree of 1 Time of drying down degree of 3 40 5 min 0,5 h 30 10 min 0,5 h 20 10 min 1 h 10 20 min 1 h 0 1 h of 30 min 2 h -5 1 h of 30 min 4 h -10 1 h of 30 min 4 h -15 1 h of 30 min 4 h -25 1 h of 30 min 4 h