ANTICORROSIVE PRIMING ENAMEL [SBE]-111 “[UNIPOL]” stamp [VU] TU 2312-001-59846005-2003 Field of application Priming enamel [SBE]-111 [UNIPOL]® stamp [VU] forms coating steadfast on Wednesday of a constant action of the diluted and concentrated inorganic acids, including of nitric (to 30%), sulfuric, salt, phosphoric, hydrofluoric and so forth, so priming enamel “OF [UNIPOL]” ® stamp [VU] is resistant down the concentrated and diluted alkalis. Priming enamel is intended for the anticorrosive protection of steel and concrete constructions. Preparation of the steel surface From welded joints to clean the welding slag (flux) and the layers of slag. By grinding to remove incisions, burrs, welding drops, to round off sharp edges, angles, teeth, the welds. For the removal of the interfering layers it is possible to use scrapers, chisels. Work should be performed in such a way as not to disrupt weld strength. The metallic surface of the constructions, which are subject down protection, it is necessary to clean down the degree Of s[a] 2,5 - Sa3 (ISO 8501-1). Putting conditions Priming enamel is allowed to bring with the ambient temperature and painted surface from 0o[S] to 35o[S] and the high relative humidity of air. Method of the putting Priming enamel can be brought by brush, by roller, by the methods of airless and air-stream atomization. Specific special features The recommended thickness of coatings is 300-500 m depending on operating conditions. The theoretical flow rate of enamel for one layer 100 m composes 0,34 [kg]/[m]2. Practical expenditure depends on many factors: the equipment used, the degree of preparation and complexity (form) of surface, weather conditions, qualification of personnel and so forth Expenditure, the thickness of the coating The recommended thickness of coatings is 300-500 m depending on operating conditions. The theoretical flow rate of enamel for one layer 100 m composes 0,34 [kg]/[m]2. Practical expenditure depends on many factors: the equipment used, the degree of preparation and complexity (form) of surface, weather conditions, qualification of personnel and so forth Ambient temperature, °[S] Time, ch -25 2 -10 2 -5 2 0 1 +20 to +35 less than 1 The time of interlamination drying indicated depends on number of the factors: the diluent used, the air circulation, ambient temperature, thicknesses film and the like and considerably it decreases with grow prettier ventilation, also, before open air. The complete set of physicomechanical properties occurs during 10-12 days (t=20oC, [f]=65%). Preparation of enamel at the point of the work Before the application of a component of enamel thoroughly intermix throughout entire volume and they mix up before the relationship 19:1 (it [komponet] №1: the component of №2) off the mass. The obtained paint must be uniform before the color and the consistency. Before the putting to maintain not less than 10 minutes. Of for achievement necessary viscosity is allowed the dilution of enamel to 10% of the total volume. Acetone or butyl acetate are used as the diluents. Cleaning container, tool Acetone is used. Storage Not to heat. To take care from the fire. Composition to store before the solidly closed container, protecting from the action of heat, straight solar rays. Guarantee period of storage before the hermetically sealed container of manufacturing plant - twelve months based on the day of production. For obtaining the additional information for the sake of the putting, the quality of surface preparation or in the case of obtaining the negative results during putting of priming enamel, to be turned at the point of the detailed consultation down the supplier