ANTICORROSIVE PRIMING ENAMEL [SBE]-111 “[UNIPOL]” stamp V -[Se] TU 2312-001-59846005-2003 Field of application Priming enamel [SBE]-111 [UNIPOL]® stamp V -[Se] forms the coating, steadfast in the atmosphere of the industrial medium of that moderated and cold climatic zones, and also to the aggressive media (solutions of alkalis), to the petroleum products (petroleum products, lubricating oils, crude oil). Priming enamel is intended for the corrosion protection of steel constructions, external surfaces of tanks and conduits, it is possible to use this coating for painting transportation means. Also coating has high decorative properties, it is stable to the washing solutions. Preparation of the steel surface From welded joints to clean the welding slag (flux) and the layers of slag. By grinding to remove incisions, burrs, welding drops, to round off sharp edges, angles, teeth, the welds. For the removal of the interfering layers it is possible to use scrapers, chisels. Work should be performed in such a way as not to disrupt weld strength. The metallic surface of the constructions, which are subject down protection, must be cleaned down the degree of cleaning S[a] 2,5 (ISO 8501-1). With the fulfillment anticorrosive of the protection of noncritical constructions is permissible the use of cleaning metallic surface down the degree St of 3 according to ISO 8501-1. Putting conditions Priming enamel is allowed to bring with the ambient temperature and painted surface from 0o[S] to 40o[S] and the relative humidity of air not more than 80%. Method of the putting Priming enamel can be brought by brush, by roller, by the methods of airless and air-stream atomization. Expenditure, the thickness of the coating The recommended thickness of coatings is 120-140 m depending on operating conditions. The theoretical flow rate of enamel for one layer 100 m composes tentatively 0,27 [kg]/[m]2. Practical expenditure depends on many factors: the equipment used, the degree of preparation and complexity (form) of surface, weather conditions, qualification of personnel and so forth Method of the putting: “wet on the wet”. The complete set of the physicomechanical properties of the coating with a thickness of 100 m, occurs during 7-8 days (t=20oC, [f]=65%). Viability after the mixing Ambient temperature, °[S] Time, ch 40 2 20 4 10 4 0 12 Preparation of enamel at the point of the work Before the application of a component of enamel thoroughly they intermix throughout entire volume and mix up before the relationship 10:1 off the mass, to thoroughly mix mixture throughout entire volume for the sake of the use of a manual or mechanical tool. Priming enamel must be uniform before the color and the consistency. Sediment on the bottom of container is not allowed. Before the putting priming enamel it is necessary to maintain not less than 10 minutes. Of for achievement necessary viscosity is allowed the dilution of priming enamel to 15% of the total volume. Xylene or solvent are used as the diluents. However, if necessary, is possible the dilution of priming enamel more than down 15%. Cleaning container, tool Are used xylene, butyl acetate, toluene, R -4. Storage Not to heat. To take care from the fire. Composition to store before the solidly closed container, protecting from the action of heat, the straight lines of the solar of rays and moisture. Guarantee period of storage before the hermetically sealed container of manufacturing plant - twelve months based on the day of production. For obtaining the additional information for the sake of the putting, the quality of surface preparation or in the case of obtaining the negative results during putting of priming enamel, to be turned at the point of the detailed consultation down the supplier