“[UNIPOL]- waterproofing” TU 2312-001-59846005-2003 Field of application Paste is intended for the waterproofing in the buildings of different designation due to all climatic conditions, the device of new and repair of the existing roofings, and also for the corrosion protection of metal constructions, technological equipment and conduits. Waterproofing possesses resistance to UV to irradiation. Preparation of the concrete surface Concrete surface must be flat, clean and dry. According to SNIP (Construction norms and regulations) 3.04.03 the humidity of concrete is allowed not more than 4%. The surface of concrete must be evened and removed based on it lime milk, upper fragile layer of concrete and remainders of old coatings. After the surface treatment it is necessary to remove dust, sand, swarf and other pollution from the zone of painting. The presence on the concrete of the spots of the machine oil or other chemical compositions is inadmissible. Putting conditions waterproofing it is allowed to bring at an ambient temperature and painted surface from 0o[S] to 35o[S]. The method of putting putting paste is possible by the method of free pouring in, with the aid of the spatula or the roller, the brush, and also by airless dispersion. Expenditure, the thickness of the coating Thickness coatings and, correspondingly, the expenditure of material are determined as far as the field of application, for example, for the roofing works it is recommended the thickness of 2-2,5 mm, for anticorrosive and chemically resistant coatings - 0,3 - 1,0 mm. Tentative expenditure of the paste: the roofing works: depending on a constructive solution of roofing - not less than 4 [kg]/[m]2. Is allowed the application of paste as the pasting material with the device of roofing with the use of roll materials (Ruberoid the like); the moisture-proof works: depending on the pressure head - 3-6 [kg]/[m]2; the corrosion protection: depending on the type of the protected object and aggressiveness of medium - 0,8-6 [kg]/[m]2. Time of the interlamination drying The time of drying the film of 300[mkm] at a temperature (20±2) of o[S] with the relative humidity of air (65±5)% down the degree “of 3” - is not more than 2 hours. The time of interlamination drying indicated is given tentative, it depends on number of the factors: the diluent used, the air circulation, ambient temperature, thicknesses film and the like and considerably it decreases with grow prettier ventilation, also, before open air. The complete set of the physicomechanical properties of the coating with a thickness of 400 m, occurs during 15 days (t=20oC, [f]=65%). Preparation for waterproofing at the point of the work Before the application to thoroughly mix waterproofing throughout entire volume with the use of a manual or mechanical tool. Waterproofing must be uniform before the color and the consistency. Sediment on the bottom of container is not allowed. Before the putting waterproofing it is necessary to maintain not less than 10 minutes. Of for achievement necessary viscosity is allowed the dilution of waterproofing to 10-15% of the total volume. As the diluents are used xylene, solvent or toluene. However, if necessary, is possible the dilution of waterproofing more than down 15%. Cleaning container, tool Are used solvent, xylene, toluene. Storage Not to heat. To take care from the fire. Composition to store before the solidly closed container, protecting from the action of heat, the straight lines of the solar of rays and moisture. Guarantee period of storage before the hermetically sealed container of manufacturing plant - six months based on the day of production. For obtaining the additional information for the sake of the putting, the quality of surface preparation or in the case obtaining negative results during putting of waterproofing, be turned at the point of the detailed consultation down the supplier.