Chemically resistant priming enamel [SBE]-111 [UNIPOL]® stamp XO Priming enamel [SBE]-111 [UNIPOL]® stamp CW (Chemical Weapons) is intended for the corrosion protection of steel constructions. Is formed weatherproof coating before the conditions of the industrial atmosphere of the moderate and cold climate. Coating wear-resistant, maintains the short-term action of sea water, lubricating oils and petroleum products, and also dry mineral fertilizers. Index Value Connecting basis: Polyurethane modified Composition: two-component, the relationship of mixing 100:7 off the mass The dry residue: Not less than 55% The relative viscosity of enamel at a temperature (20±0,5) of °C on the viscosimeter of the type Of [v]3-246 (or [VZ]-4) with the diameter of nozzle 4 mm: Is not less than 90 s Degree of the grinding: Not are more than 50 m Color: Any about the agreement for the sake of the customer or on catalog RAL Degree of the dilution: 10-15% of the total volume Storage Not to heat. To take care from the fire. Composition to store before the solidly closed container, protecting from the action of heat, the straight lines of the solar of rays and moisture. Guarantee period of storage before the hermetically sealed container of manufacturing plant - six months based on the day of production. Diluents: R -4, xylene Putting: By brush, by roller, by the methods pneumo- and airless dispersion Quantity of the layers: 2-3 depending on the aggressiveness of the medium Expenditure and the thickness of the coating: With the recommended thickness of coating ~ 240 m The theoretical flow rate ~ of 0,570 [kg]/[m]2 Putting conditions Priming enamel is allowed to bring at an ambient temperature and painted surface from minus of 10o[S] to 35o[S] and high relative humidity of air. Is possible forced drying in the drying chambers at a temperature not more than 60 o[S] The time of drying the coating with a thickness of 100 m at a temperature (20±2) of o[S] and [f]=65% down the degree “of 3” according to GOST 19007, is not more 1 the hour The complete set of the physicomechanical properties of the coating with a thickness of 240 m at a temperature of 20oC and relative humidity of air 65% 5 days Index Value The exterior view of the coating Uniform semigloss surface without the foreign inclusions Wear resistance of coating according to GOST 20811-75 (method a) 3,3 kgf/m Strength of film with the bend not more than 1 mm Adhesion, according to GOST 15140-78 method 2 is not more than 1 mark Strength of film with the impact not less than 50 cm Hiding power of the dried coating not more than 60 [g]/[m]2 Hardness about the pendulum gravimeter M-3 not less than 0,3 conv. un. The resistance of film to static action by 3% of solution of sodium hydroxide with (20±2)°[S], the thickness of film is 240 m not less than 48 hours The resistance of film to static action by 30% of solution of sodium hydroxide with (20±2)°[S], the thickness of film is 240 m not less than 72 hours The resistance of film to the static action of water with (20±2)°[S], thickness of the layer is 240 m not less than 96 hours Durability of film (thickness of film 140 m) to the static action with (20±2)°[S], the petroleum products the diesel fuel the crude oil the petroleum residue not less than 96 hours Surface preparation Basis Surface preparation C[tal] down the degree of cleaning S[a] 2,5 (ISO 8501-1) Good results are achieved by surface preparation down the degree St of 3 on ISO 8501-1. Safety engineering: With conducting of internal work, and after their end thoroughly to also air accomodation. To use individual protective means (TU 2312-001-59846005-2003). The authenticity of present data is based beyond the laboratory tests and the practical experience. As supplier firm cannot bear responsibility for the damage, substituted by the application of material not in accordance with the given out by firm instruction beyond the application or with the use about the incorrect designation. Each individual case of applying the material is individual. Specifications description does not free based on fulfilling of the acting normative requirements of construction legislation. This technical description loses force after the appearance of a new editorial staff of text. The reprinting of texts and illustrations, the quoting of materials are allowed only by written authorization of the authors.