Chemically resistant priming enamel [SBE]-111 [UNIPOL]® stamp [VU] Priming enamel [SBE]-111 [UNIPOL]® stamp [v] forms coating steadfast on Wednesday of a constant action of the diluted and concentrated inorganic acids, including of nitric (to 30%), sulfuric, salt, phosphoric, hydrofluoric and so forth, so priming enamel [SBE]-111 “OF [UNIPOL]” ® stamp [VU] is resistant down the concentrated and diluted alkalis. Priming enamel is intended for the anticorrosive protection of steel and concrete constructions. Index Value Connecting basis: Fluorineepoxy Composition: Two-component; 19:1 off the mass The dry residue: Not less than 50% The relative viscosity of enamel after mixing of components at a temperature (20±0,5) of °C on the viscosimeter of the type Of [v]3-246 (or [VZ]-4) with the diameter of nozzle 4 mm: Is not less than 90 s Degree of the grinding: Not are more than 40 m Color: Any about the agreement for the sake of the customer or on catalog RAL Degree of the dilution: 10-15% of the total volume Storage Not to heat. To take care from the fire. Composition to store before the solidly closed container, protecting from the action of heat, the straight lines of the solar of rays and moisture. Guarantee period of storage before the hermetically sealed container of manufacturing plant - twelve months based on the day of production. Diluents: Butyl acetate, acetone Putting: By brush, by roller, by the methods pneumo- and airless dispersion Quantity of the layers: 4-6 depending on the aggressiveness of the medium Expenditure and the thickness of the coating: With the recommended thickness of coating 300-500 m The theoretical flow rate ~ of 1,02-1,75 [kg]/[m]2 Putting conditions Priming enamel is allowed to bring with the ambient temperature and painted surface from 0[oS] to 35o[S] and the high relative humidity of air. Viability, is not less 48 hours after the mixing of the components The time of drying the coating with a thickness of 80 m at a temperature (20±2) of wasps and [f]=65% down the degree “of 3” according to GOST 19007, is not more 1 the hour The complete set of the physicomechanical properties of coating at a temperature of 20[o]C and relative humidity of air 65% 7-8 days Index Value The exterior view of the coating Uniform lusterless surface without the foreign inclusions Wear resistance of coating according to GOST 20811-75 (method a) 3,3 kgf/m Strength of film with the bend not more than 1 mm Adhesion, according to GOST 15140-78 method 2 is not more than 1 mark Strength of film with the impact not less than 50 cm Hiding power of the dried coating not more than 60 [g]/[m]2 Hardness about the pendulum gravimeter M-3 not less than 0,3 conv. un. The resistance of film to static action by 50% of solution of sulfuric acid with (50±5)°[S], the thickness of coating is 500 m not less than 48 hours The resistance of film to the static action of chromic acid mixture with (20±5)°[S], the thickness of coating is 500 m not less than 48 hours The resistance of film to the static action of mixture 35% HCl and 5%HF with (20±5)°[S], the thickness of coating is 500 m not less than 48 hours The resistance of film to static action to solution 30% HNO3 with (20±5)°[S], the thickness of coating is 500 m not less than 48 hours Surface preparation Basis Surface preparation C[tal]: down the degree of cleaning S[a] 2,5 (ISO 8501-1) Safety engineering: With conducting of internal work, and after their end thoroughly to also air accomodation. To use individual protective means (TU 2312-001-59846005-2003). The authenticity of present data is based beyond the laboratory tests and the practical experience. As supplier firm cannot bear responsibility for the damage, substituted by the application of material not in accordance with the given out by firm instruction beyond the application or with the use about the incorrect designation. Each individual case of applying the material is individual. Specifications description does not free based on fulfilling of the acting normative requirements of construction legislation. This technical description loses force after the appearance of a new editorial staff of text. The reprinting of texts and illustrations, the quoting of materials are allowed only by written authorization of the authors.