Atmosphere - and oil and gasoline resistant priming enamel [UNIPOL]® stamp V -[Se] Priming enamel [UNIPOL]® stamp V -[Se] forms the coating, steadfast in the atmosphere of the industrial medium of that moderated and cold climatic zones, and also to the aggressive media (solutions of alkalis), to the petroleum products (petroleum products, lubricating oils, crude oil). Priming enamel is intended for the corrosion protection of steel constructions, external surfaces of tanks and conduits, it is possible to use this coating for painting transportation means. Also coating has high decorative properties, it is stable to the washing solutions. Index Value Connecting basis: Siliconeepoxy modified Composition, the relationship of the components: Two-component; 10:1 off the mass The dry residue: 60-65% The relative viscosity of enamel at a temperature (20±0,5) of °C on the viscosimeter of the type Of [v]3-246 (or [VZ]-4) with the diameter of nozzle 4 mm: 90-120 it flogged Degree of the grinding: less than 40 m Color: Any about the agreement for the sake of the customer or on catalog RAL Degree of the dilution: to 15% of the total volume Storage Not to heat. To take care from the fire. Composition to store before the solidly closed container, protecting from the action of heat, the straight lines of the solar of rays and moisture. Guarantee period of storage before the hermetically sealed container of manufacturing plant - twelve months based on the day of production. Diluents: Xylene, butyl acetate, toluene, R -4 Putting: By brush, by roller, by the methods pneumo- and airless dispersion Method of the putting: “wet on the wet”. Quantity of the layers: 1-2 depending on the aggressiveness of the medium Expenditure and the thickness of the coating: With the recommended thickness of coating 120-140 m The theoretical flow rate ~ of 0,32-0,37 [kg]/[m]2 Putting conditions Priming enamel is allowed to bring with the ambient temperature and painted surface from 0o[S] to 40o[S] and the relative humidity of air not more than 80%. Viability after mixing, ch: with 40±20[S] with 20±20[S] with 10±20[S] with 00[S] 2 4 4 12 The complete set of the physicomechanical properties of the coating with a thickness of 100 m at a temperature of 20oC and relative humidity of air 65% with 40±20[S] with 20±20[S] with 10±20[S] with 00[S] 10 days Index Value The exterior view of the coating Uniform semigloss surface without the foreign inclusions Wear resistance of coating according to GOST 20811-75 (method a) 3,2 kgf/m Strength of film with the bend not more than 2 mm Adhesion, according to GOST 15140-78 method 2 1 mark Strength of film with the impact not less than 40 cm Hiding power of the dried coating not more than 100 [g]/[m]2 0,4 Specific volumetric electrical resistance of coating pv, [Om]*[sm] 3,14*1014 The resistance of film to static action by 3% of solution Of n[aS]l with (50±5)°[S], the thickness of coating is 150 m not less than 48 hours The resistance of film to static action by 3% of solution Of n[aS]l with (20±2)°[S], the thickness of coating is 140 m not less than 72 hours The resistance of film to static action by 30% of solution of sodium hydroxide with (20±2)°[S], the thickness of film is 140 m not less than 72 hours Durability of film (thickness of film 140 m) to the static action with (20±2)°[S] the petroleum products the diesel fuel the crude oil the petroleum residue not less than 96 hours The resistance of film to the static action of water with (20±2)°[S], thickness of the layer is 140 m not less than 48 hours Surface preparation: Basis Surface preparation Steel down the degree of cleaning S[a] 2,5 (ISO 8501-1), is allowed with the fulfillment anticorrosive of the protection of noncritical constructions down the degree of cleaning St 3 (ISO 8501-1). Safety engineering: With conducting of internal work, and after their end thoroughly to also air accomodation. To use individual protective means (TU 2312-001-59846005-2003). The authenticity of present data is based beyond the laboratory tests and the practical experience. As supplier firm cannot bear responsibility for the damage, substituted by the application of material not in accordance with the given out by firm instruction beyond the application or with the use about the incorrect designation. Each individual case of applying the material is individual. Specifications description does not free based on fulfilling of the acting normative requirements of construction legislation. This technical description loses force after the appearance of a new editorial staff of text. The reprinting of texts and illustrations, the quoting of materials are allowed only by written authorization of the authors.