Chemically resistant priming enamel [SBE]-111 [UNIPOL]® stamp [VE] Priming enamel [SBE]-111 [UNIPOL]® stamp [VE] forms chemically resistant coating to such media as the concentrated and dilute acids and alkalis and to a number of oxidizers (chromates, dichromates, permanganates so forth). Priming enamel is intended for the anticorrosive protection of steel constructions and concrete surfaces. Index Value Connecting basis: Natural rubber- resin modified Composition: Single-component, ready to the application The dry residue: Not less than 45% The relative viscosity of enamel at a temperature (20±0,5) of °C on the viscosimeter of the type Of [v]3-246 (or [VZ]-4) with the diameter of nozzle 4 mm: Is not less than 90 s Degree of the grinding: Not are more than 50 m Color: Any about the agreement for the sake of the customer or on catalog RAL Degree of the dilution: 10-15% of the total volume Storage Not to heat. To take care from the fire. Composition to store before the solidly closed container, protecting from the action of heat, the straight lines of the solar of rays and moisture. Guarantee period of storage before the hermetically sealed container of manufacturing plant - six months based on the day of production. Diluents: Xylene, solvent, toluene Putting: By brush, by roller, by the methods pneumo- and airless dispersion Quantity of the layers: 3-5 depending on the aggressiveness of the medium Expenditure and the thickness of the coating: With the recommended thickness of coating 300-500 m The theoretical flow rate ~ of 0,66-1,10 [kg]/[m]2 Putting conditions Priming enamel is allowed to bring at an ambient temperature and painted surface from minus of 25o[S] to 35o[S] and high relative humidity of air. The time of drying the coating with a thickness of 70 m at a temperature (20±2) of o[S] and [f]=65% down the degree “of 3” according to GOST 19007, is not more 1 the hour The complete set of the physicomechanical properties of coating at a temperature of 20oC and relative humidity of air 65% 10-12 days Index Value The exterior view of the coating Uniform lusterless surface without the foreign inclusions Wear resistance of coating according to GOST 20811-75 (method a) 3,3 kgf/m Strength of film with the bend not more than 1 mm Adhesion, according to GOST 15140-78 method 2 is not more than 1 mark Strength of film with the impact not less than 50 cm Hiding power of the dried coating not more than 60 [g]/[m]2 Hardness about the pendulum gravimeter M-3 not less than 0,3 conv. un. The resistance of film to static action by 37% of solution of hydrochloric acid with (50±5)°[S], the thickness of coating is 500 m not less than 48 hours The resistance of film to static action by 96% of solution of sulfuric acid with (70±5)°[S], the thickness of coating is 500 m not less than 48 hours The resistance of film to the static action of the concen. of the solution of hydrofluoric acid with (70±5)°[S], the thickness of coating is 500 m not less than 48 hours The resistance of film to the static action of the concen. of the solution of citric acid with (70±5)°[S], the thickness of coating is 500 m not less than 48 hours Surface preparation Basis Surface preparation C[tal]: down the degree of cleaning S[a] 2,5 (ISO 8501-1) Safety engineering: With conducting of internal work, and after their end thoroughly to also air accomodation. To use individual protective means (TU 2312-001-59846005-2003). The authenticity of present data is based beyond the laboratory tests and the practical experience. As supplier firm cannot bear responsibility for the damage, substituted by the application of material not in accordance with the given out by firm instruction beyond the application or with the use about the incorrect designation. Each individual case of applying the material is individual. Specifications description does not free based on fulfilling of the acting normative requirements of construction legislation. This technical description loses force after the appearance of a new editorial staff of text. The reprinting of texts and illustrations, the quoting of materials are allowed only by written authorization of the authors.