Field of application: Paste is intended for waterproofing of walls, floors in the buildings of different designation due to all climatic conditions, device of new and repair of the existing roofings, and also for the corrosion protection of metal constructions, technological equipment and conduits. Waterproofing possesses resistance to UV to irradiation. Table of №1 Index Value Connecting basis: the styrene-butadiene thermoplastics Composition Single-component, ready to the application The dry residue 50-75% Degree of the grinding Not are more than 50 m Color black Degree of the dilution 10-15% of the total volume Storage Not to heat. To take care from the fire. Composition to store before the solidly closed container, protecting from the action of heat, the straight lines of the solar of rays and moisture. Guarantee period of storage before the hermetically sealed container of manufacturing plant - six months based on the day of production. Diluents: Xylene, solvent, toluene Putting: By brush, by roller, by spatula, by the methods of the airless dispersion Quantity of the layers: 1-6 depending on the field of application Expenditure and the thickness of the coating: With the thickness of coating 100 m the theoretical flow rate ~ of 0,22 [kg]/[m]2 Putting conditions Waterproofing it is allowed to bring at an ambient temperature and painted surface from 0o[S] to 35o[S]. The time of drying the coating with a thickness of 300 m at a temperature (20±2) of o[S] and [f]=65% down the degree “of 3” according to GOST 19007, is not more 2 hours The complete set of the physicomechanical properties of the coating with a thickness of 400 m at a temperature of 20oC and relative humidity of air 65% 15 days Table of №2. Index Value The exterior view of the coating Uniform lusterless surface without the foreign inclusions Relative elongation, %, is not less 150 Conditional strength, MPa, not are less 0,6 Adhesion strength with the concrete according to GOST 28574-90, MPa, is not less: 2,8 Adhesion strength of coating to the surface according to GOST 15140 (method 4): [TSSP] Steels The sheet iron 11 11 11 Adhesion strength between layers, MPa, is not less 0.2 Thermal stability at a temperature plus of 100o[S], ch, is not more 3 Flexibility on the rod d of 10[mm], 50°[S], is not less 1 Resistance to cracks, mm 1,2 The resistance of film to static action at a temperature (20±2) of 0[S], ch, is not less: - 3%- oho solution NaCl; - the water 48 48 Water absorption for 24 h, % off the mass, is not more 2 Surface preparation: Basis Surface preparation Concrete surface On SNIP (Construction norms and regulations) 3.04.03 (see instruction beyond the putting) Safety engineering: With conducting of internal work, and after their end thoroughly to also air accomodation. To use individual protective means (TU 2312-001-59846005-2003). The authenticity of present data is based beyond the laboratory tests and the practical experience. As supplier firm cannot bear responsibility for the damage, substituted by the application of material not in accordance with the given out by firm instruction beyond the application or with the use about the incorrect designation. Each individual case of applying the material is individual. Specifications description does not free based on fulfilling of the acting normative requirements of construction legislation. This technical description loses force after the appearance of a new editorial staff of text. The reprinting of texts and illustrations, the quoting of materials are allowed only by written authorization of the authors.