Chemically resistant priming enamel [SBE]-111 [UNIPOL]® stamp [GU] Priming enamel [SBE]-111 [UNIPOL]® stamp [GU] is intended for the anticorrosive protection of steel constructions due to the conditions of the industrial atmosphere of the moderate and cold climate. The waterproof and oil and gasoline resistant covering, which maintains for a long time the action of mineral oils, gasoline, kerosene and other petroleum products, is formed. It adapts for the corrosion protection of conduits, internal and external surfaces of capacities, transportation means. Index Value Connecting basis: [uretanakrilovaya] modified Composition: Two-component, 5:1 off the mass The dry residue: 70-75% The relative viscosity of enamel at a temperature (20±0,5) of °C on the viscosimeter of the type Of [v]3-246 (or [VZ]-4) with the diameter of nozzle 4 mm: Is not less than 90 s Degree of the grinding: Not are more than 40 m Color: Any about the agreement for the sake of the customer or on catalog RAL Degree of the dilution: 10% of the total volume Storage Not to heat. To take care from the fire. Composition to store before the solidly closed container, protecting from the action of heat, the straight lines of the solar of rays and moisture. Guarantee period of storage before the hermetically sealed container of manufacturing plant - twelve months based on the day of production. Diluents: butyl acetate, solvent, toluene Putting: By brush, by roller, by the methods pneumo- and airless dispersion Quantity of the layers: 2-3 depending on the aggressiveness of the medium Expenditure and the thickness of the coating: With the recommended thickness of coating 150-200 m The theoretical flow rate ~ of 0,33-0,44 [kg]/[m]2 Putting conditions Priming enamel is allowed to bring with the ambient temperature and painted surface from 0o[S] to 35o[S] and the high relative humidity of air. Time of drying the coating with a thickness of 50 m at a temperature (20±2) of o[S] and [f]=65% down the degree “of 3” according to GOST 19007 1 hour The complete set of the physicomechanical properties of coating at a temperature of 20oC and relative humidity of air 65% 5-8 days Viability with (20±2) o[S], not less 5 Index Value The exterior view of the coating Uniform glossy surface without the foreign inclusions Strength of film with the bend not more than 1 mm Adhesion, according to GOST 15140-78 method 2 is not more than 1 mark Strength of film with the impact not less than 50 cm Hardness about the pendulum gravimeter [TML] (pendulum a) not less than 0,4 conv. un. Resistance of film to static action 3% solution N[aS]l with (20±2)°[S], film 150 m not less than 48 hours Durability of film (thickness of film 150 m) to static action by 30% of solution of sodium hydroxide with (20±2)°[S] not less than 24 hours Durability of film (thickness of film 150 m) to the static action with (20±2)°[S] of gasoline, kerosene and other petroleum products not less than 48 hours The durability of film (thickness of film 150 m) to the static action water with (20±2)°[S], thickness of the layer is 150 m not less than 48 hours Surface preparation Basis Surface preparation C[tal] down the degree of cleaning S[a] 2,5 (ISO 8501-1) Safety engineering: With conducting of internal work, and after their end thoroughly to also air accomodation. To use individual protective means (TU 2312-001-59846005-2003). The authenticity of present data is based beyond the laboratory tests and the practical experience. As supplier firm cannot bear responsibility for the damage, substituted by the application of material not in accordance with the given out by firm instruction beyond the application or with the use about the incorrect designation. Each individual case of applying the material is individual. Specifications description does not free based on fulfilling of the acting normative requirements of construction legislation. This technical description loses force after the appearance of a new editorial staff of text. The reprinting of texts and illustrations, the quoting of materials are allowed only by written authorization of the authors.