Antifouling paint is priming enamel [SBE]-111 [UNIPOL]® stamp AT Priming enamel [SBE]-111 [UNIPOL]® stamp AT forms thermoresistant and weatherproof anticorrosive coating. Antifouling paint priming enamel is intended for the anticorrosive protection of steel surfaces, technological equipment (gas-, steam pipelines, the elements of the systems of cold and hot water supply, the chimney stacks of [i].[t].[d]), which are undergone before the process of operation the action of the temperature to +200o[S]. It possesses high decorative properties. It is supplied before the complete set with the [strukturiruyushchey] additive (5% by vol) Table 1 Index Value Connecting basis: Hydrocarbon- silicone Composition: Single-component, ready to the application The dry residue: not less than 50% Color: Any about the agreement for the sake of the producer The relative viscosity of enamel at a temperature (20±0,5) of °C on the viscosimeter of the type Of [v]3-246 (or [VZ]-4) with the diameter of nozzle 4 mm: Is not less than 90 s Degree of the grinding: Not are more than 50 m Degree of the dilution: 10-15% of the total volume Storage Not to heat. To take care from the fire. Composition to store before the solidly closed container, protecting from the action of heat, the straight lines of the solar of rays and moisture. Storage conditions according to GOST 9980.5. Guarantee period of storage before the hermetically sealed container of manufacturing plant - 6 months based on the day of production. Diluents: Xylene, solvent, toluene Putting: By brush, by roller, by the methods pneumo- and airless dispersion Quantity of the layers: 2-4 depending on the aggressiveness of the medium Expenditure and the thickness of the coating: With the recommended thickness of coating 140-160 m The theoretical flow rate ~ of 0,31-0,35 [kg]/[m]2 Putting conditions Priming enamel is allowed to bring at an ambient temperature and painted surface from minus of 10o[S] to 35o[S] and high relative humidity of air. The time of drying the coating with a thickness of 70 m at a temperature (20±2) of o[S] and f 65% down the degree “of 3” according to GOST 19007, is not more 1 hour The complete set of the physicomechanical properties of coating with temperature 20 oC and relative humidity of air 65% 5-6 days Table 2 Index Value The exterior view of the coating Uniform lusterless surface Wear resistance of coating according to GOST 20811-75 (method a) 3,3 kgf/m Strength of film with the bend not more than 1 mm Adhesion, according to GOST 15140-78 method 2 is not more than 1 mark Strength of film with the impact not less than 50 cm Hiding power of the dried coating not more than 60 [g]/[m]2 Hardness about the pendulum gravimeter M-3 not less than 0,21 conv. un. Heat resistance of coating with 200o[S] 3 hours Surface preparation: Table 3 Basis Surface preparation C[tal]: down the degree of cleaning S[a] 2,5 (ISO 8501-1) Safety engineering: With conducting of internal work, and after their end thoroughly to also air accomodation. To use individual protective means (TU 2312-001-59846005-2003). The authenticity of present data is based beyond the laboratory tests and the practical experience. As supplier firm cannot bear responsibility for the damage, substituted by the application of material not in accordance with the given out by firm instruction beyond the application or with the use about the incorrect designation. Each individual case of applying the material is individual. Specifications description does not free based on fulfilling of the acting normative requirements of construction legislation. This technical description loses force after the appearance of a new editorial staff of text. The reprinting of texts and illustrations, the quoting of materials are allowed only by written authorization of the authors.