Priming enamel “OF [UNIPOL]” stamp AP Closegrained feeding coating of the sex Priming enamel [SBE]-111 “OF [UNIPOL] " ® stamp AP is intended for the putting beyond any mineral surface (concrete, brick, plastering, putty so forth) and surface protection from the mechanical and chemical actions. Priming enamel [SBE]-111 [UNIPOL]® stamp AP adapts for the device of closegrained seamless outdoor coatings before the accomodations of industrial and civil designation with the average mechanical loads. Index Value Connecting basis: Vinyl polymers and aromatic resins Composition: Single-component, ready to the application The dry residue: 50-55% The relative viscosity of enamel at a temperature (20±0,5) of °C on the viscosimeter of the type Of [v]3-246 (or [VZ]-4) with the diameter of nozzle 4 mm: 100-150 it flogged Degree of the grinding: Not are more than 50 m Color: Any about the agreement for the sake of the customer or on catalog RAL Degree of the dilution: 10-15% of the total volume Storage: Not to heat. To take care from the fire. Composition to store before the solidly closed container, protecting from the action of heat, the straight lines of the solar of rays and moisture. Guarantee period of storage before the hermetically sealed container of manufacturing plant - six months based on the day of production. Diluents: Xylene, solvent, toluene Putting: By brush, by roller, by the airless dispersion Quantity of the layers: 2-5 depending on mechanical load and aggressiveness of the medium Discharge and the thickness of the coating: With the recommended thickness of coating 400-700[mkm]. The theoretical flow rate ~ of 1,1-1,9 [kg]/[m]2. Putting conditions Priming enamel is allowed to bring at an ambient temperature and painted surface from 0o[S] to 35o[S]. The time of drying the coating with a thickness of 100 m at a temperature (20±2) of 0[S] and [f]=65% down the degree “of 3” according to GOST 19007, is not more 1 hour The complete set of the physicomechanical properties of the coating with a thickness of 400-700 m at a temperature of 20oC and relative humidity of air 65% 14 days Index Value The exterior view of the coating Uniform semigloss surface without the foreign inclusions Wear resistance of coating according to GOST 20811-75 (method a) 5,5 kgf/m Adhesion, according to GOST 15140-78 method 2 is not more than 1 mark (on the concrete) Strength of film with the impact not less than 50 cm Hiding power of the dried coating not more than 60 [g]/[m]2 Hardness about the pendulum gravimeter M-3 not less than 0,33 conv. un. The resistance of film to static action by 3% of solution Of n[aS]l with (50±5) o[S], the thickness of coating is 150 m not less than 48 hours Surface preparation: Index Value Concrete surface On SNIP (Construction norms and regulations) 3.04.03 (see instruction beyond the putting) Safety engineering: With conducting of internal work, and after their end thoroughly to also air accomodation. To use individual protective means (TU 2312-001-59846005-2003). The authenticity of present data is based beyond the laboratory tests and the practical experience. As supplier firm cannot bear responsibility for the damage, substituted by the application of material not in accordance with the given out by firm instruction beyond the application or with the use about the incorrect designation. Each individual case of applying the material is individual. Specifications description does not free based on fulfilling of the acting normative requirements of construction legislation. This technical description loses force after the appearance of a new editorial staff of text. The reprinting of texts and illustrations, the quoting of materials are allowed only by written authorization of the authors.