Weatherproof priming enamel [SBE]-111 [UNIPOL]® stamp ATs Priming enamel [SBE]-111 [UNIPOL]® stamp ATs - [odnoupakovochnaya] zinc-filled composition, intended for the anticorrosive protection of the steel, concrete and zinc-coated surfaces. Composition contains the highly dispersed powder of zinc, natural rubber- resin bonding agent, organic solvents and contributions of auxiliary substances. Coating is used as the priming coating with a thickness of up to 80 m, overlapped for the sake of other paints. Coating does not influence the mechanical properties of the weld, it easily yields to repair and restoration by cleaning and putting the new layer in the place of damage. Coating works in the atmosphere of the industrial medium of that moderated and cold climatic zones. Index Value Connecting basis: Natural rubber- resin modified Composition: Single-component, ready to the application The dry residue Not less than 75% Content of zinc: 89-95% The relative viscosity of enamel at a temperature (20±0,5) of °C on the viscosimeter of the type Of [v]3-246 (or [VZ]-4) with the diameter of nozzle 4 mm: 90-150 it flogged Degree of the grinding Not are more than 50 m Color: Gray Degree of the dilution: 10-15% of the total volume Storage: Not to heat. To take care from the fire. Composition to store before the solidly closed container, protecting from the action of heat, the straight lines of the solar of rays and moisture. Guarantee period of storage before the hermetically sealed container of manufacturing plant - six months based on the day of production. Diluents: Xylene, solvent, toluene Putting: By brush, by roller, by the methods pneumo- and airless dispersion Quantity of the layers: 1 as the base coat Expenditure and the thickness of the coating: With the recommended thickness of coating 70-80 m The theoretical flow rate ~ of 0,20-0,23 [kg]/[m]2 Putting conditions Priming enamel is allowed to bring at an ambient temperature and painted surface from minus of 25o[S] to 35o[S] and relative humidity of air not more than 90%. The time of drying the coating with a thickness of 70 m at a temperature (20±2) of o[S] and [f]=65% down the degree “of 3” according to GOST 19007, is not more 1 hour The complete set of the physicomechanical properties of the coating with a thickness of 70 m at a temperature of 20oC and relative humidity of air 65% 4-5 days Index Value The exterior view of the coating Uniform lusterless surface without the foreign inclusions Wear resistance of coating according to GOST 20811-75 (method a) 3,3 kgf/m Strength of film with the bend not more than 1 mm Adhesion, according to GOST 15140-78 method 2 the mark is not more than 2 Strength of film with the impact not less than 50 cm Hiding power of the dried coating not more than 60 [g]/[m]2 Hardness about the pendulum gravimeter M-3 not less than 0,3 conv. un. The resistance of film to static action by 3% of solution Of n[aS]l with (50±5)°[S], the thickness of coating is 150 m not less than 48 hours Surface preparation: Basis Surface preparation C[tal]: down the degree of cleaning S[a] 2,5 (ISO 8501-1) Safety engineering: With conducting of internal work, and after their end thoroughly to also air accomodation. To use individual protective means (TU 2312-001-59846005-2003). The authenticity of present data is based beyond the laboratory tests and the practical experience. As supplier firm cannot bear responsibility for the damage, substituted by the application of material not in accordance with the given out by firm instruction beyond the application or with the use about the incorrect designation. Each individual case of applying the material is individual. Specifications description does not free based on fulfilling of the acting normative requirements of construction legislation. This technical description loses force after the appearance of a new editorial staff of text. The reprinting of texts and illustrations, the quoting of materials are allowed only by written authorization of the authors.