Protocol of the monitoring tests of № 22 from 30.06.2001.[g].
Base for conducting the tests agreement 4-596/25 from 30.03.2001 g.  Designation of production the coating: [SBE]-111 “Of [unipol]” stamp B
Testing at the point of possibility of applying the coating [SBE]-111 “Of [unipol]” stamp B for the corrosion protection of metal constructions of sea water-engineering and coast constructions, in particular during overload and storage of the mineral fertilizers.
Date of obtaining the models: 12.04.2001 g., 1 kgf
Information about the tested models the viscous fluid of dark color, applied down the protected surface by brush, by roller or by the dispersion
Registration number: S, IS OTHER
Test procedure: Procedure of accelerated tests (YAKUT 25-029-96)
Date of the tests of models on May 18 - on June 29, 2001.
General conclusion: the coating [SBE]-111 “Of [unipol]” stamp B can be [rekomendovano] for the corrosion protection of the metal structures of the sea water-engineering and coast constructions, including of those intended for the overload and storage of the mineral fertilizers.
Heads by division 25, Candidate of Technical Sciences, [st].[n].[s]. [G].[V]. Of [markozov]
Heads by sector 252, Candidate of Technical Sciences, [st].[n].[s]. [YU].[E]. Of [zobachev]
St. scientific colleagues, the Candidate of Technical Sciences OF [E].[V]. [Sominskaya]
The scientific worker OF [L].[N]. Of [lenkova]
Application to the protocol of the monitoring tests of № 22 from 30.06.2001 g.
Results of the tests of coating “[Unipol] B [SBE]-111” to the action of the mineral fertilizers.
| The medium being investigated |
Thickness of the initial layer of the products of corrosion, MKM |
Thickness of coating, which includes the thickness of the layer of the products of corrosion, MKM |
Estimation of coating state according to GOST 9.407-83 (mark) with the duration of tests, twenty-four hours |
| 1 |
3 |
10 |
20 |
30 |
| Chloride potassium is ALL-UNION STATE STAN. 4568-83 |
50-70 |
500-550 |
1 |
1 |
1 |
1 |
1 |
| 560-680 |
1 |
1 |
1 |
1 |
1 |
| Carbamide is ALL-UNION STATE STAN. 2081-75 |
50-70 |
480-580 |
1 |
1 |
1 |
1 |
1 |
| 570-690 |
1 |
1 |
1 |
1 |
1 |
| Ammophos is ALL-UNION STATE STAN. 18918-85 |
50-70 |
510-610 |
1 |
1 |
1 |
1 |
1 |
| 570-690 |
1 |
1 |
1 |
1 |
1 |
| Ammonium sulfate ALL-UNION STATE STAN. 9097-82 |
50-70 |
490-640 |
1 |
1 |
1 |
1 |
1 |
| 550-660 |
1 |
1 |
1 |
1 |
1 |
Results of determining the adhesive strength of coating “[Unipol] B [SBE]-111”
| Designation of the coating |
Thickness of the initial layer of the products of corrosion, MKM |
Thickness of coating, which includes the thickness of the layer of the products of corrosion, MKM |
Adhesion about the method of normal detachment on ISO 4624 |
| Value of breaking load, MPa |
Form of fracture of the model |
| [Unipol] B [SBE]-111 |
50-70 |
400-520 |
1,00 |
Inside the covering down 50-70% of surface and On the Border metal with the coating |
| 1,00 |
| 1,00 |
| 1,00 |
| 420-550 |
0,75 |
Inside the covering down 20-30% of surface and inside the layer of rust |
| 0,80 |
| 0,80 |
| 0,80 |
Results of determining the adhesive strength of coating “[Unipol] B [SBE]-111” after tests to the action of the mineral fertilizers
| The medium being investigated |
Thickness of the initial layer of the products of corrosion, MKM |
Thickness of coating, which includes the thickness of the layer of the products of corrosion, MKM |
Adhesion about the method of normal detachment on ISO 4624 |
| Value of breaking load, MPa |
Form of fracture of the model |
| Chloride potassium is ALL-UNION STATE STAN. 4568-83 |
50-70 |
520-580 |
1,00 |
Inside the covering and On the Border metal with the coating |
| 1,00 |
| 1,00 |
| 1,00 |
| 520-560 |
0,75 |
Inside the covering and inside the layer of rust |
| 1,00 |
| 0,75 |
| 1,00 |
| Carbamide is ALL-UNION STATE STAN. 208 1-75 |
50-70 |
480-620 |
1,10 |
Inside the covering and On the Border metal with the coating |
| 1,20 |
| 1,10 |
| 1,00 |
| 570-620 |
1,00 |
Inside the covering and inside the layer of rust |
| 1,00 |
| 0,80 |
| 0,90 |
| Ammophos is ALL-UNION STATE STAN. 18918-85 |
|
400-660 |
1,10 |
Inside the covering and On the Border metal with the coating |
| 0,80 |
| 0,90 |
| 0,70 |
| 510-740 |
1,00 |
Inside the covering and inside the layer of rust |
| 0,70 |
| 0,70 |
| 1,20 |
| Ammonium sulfate ALL-UNION STATE STAN. 9097-82 |
50-70 |
480-620 |
1,00 |
Inside the covering and On the Border metal with the coating |
| 0,80 |
| 1,20 |
| 0,90 |
| 570-640 |
0,80 |
Inside the covering and inside the layer of rust |
| 0,80 |
| 0,80 |
| 1,10 |
|
Producer