Conclusion about the results of tests to [pokryti] on the basis of the enamel [SBE]-111 [UNIPOL]®
- Are carried out the tests of the painter- technological, physicomechanical and shielding properties of coatings on the basis of the enamel [SBE]-111 “OF [UNIPOL]” of stamp.
- the Painter- technological properties of enamel are satisfactory: enamel is single-component, it does not have the firm, difficultly mixed deposit after storage, it is prepared at the point of the work only by bringing to the working viscosity, is brought well by the method of air-stream atomization.
- Coatings on the basis of the enamel [SBE]-111 “OF [UNIPOL]”, substituted down the surfaces, purified of oxides by shot-blast method to degree of 2 according to GOST 9.402-80, possess the high physicomechanical properties: by strength with the impact according to GOST 4765-73 - 50 cm and by adhesion about the method of lattice cuts according to GOST 15140 - 78 - 1 mark. The coating “FOR THE SAKE OF [UNIPOL]” possesses low hardness about the pendulum gravimeter [ME]-3 according to GOST 5233-89 - 0,07 before the relative units and in 10 days collects 0,1 rel. un. the resistance of coating to abrasion high and it is 3,3 kgf/m.
- On the basis the analysis of the results of tests according to GOST 9.401-91 (method 5) the period of the service of the two-layered coatings [SBE]-111 “OF [UNIPOL]” with the thickness of 180 m, substituted down the surface purified of oxides by shot-blast method to degree of 2 according to GOST 9.402-80, due to the conditions of the industrial atmosphere of the moderate climate is 10 years.
- The high physicomechanical properties of the coatings “FOR THE SAKE OF [UNIPOL]” can be achieved even by minimum abrasive surface preparation without the degreasing.
- The decorative properties of the coatings through 45 cycles of tests according to GOST 9.401-91 (method 5), which corresponds to operation in the open atmosphere of the moderate climate for 6 years with the presentation of the increased requirements at the point of the decorative form.
- Coatings on the basis of the enamel [SBE]-111 “OF [UNIPOL]” with the thickness of 180 m, substituted down the surfaces, purified of oxides by shot-blast method to degree of 2 according to GOST 9.402-80, possess high durability before the distilled water (more than 180 days of tests without a change in the shielding properties) and relatively high - before the 3% the solution of chloride sodium (90 days without a change in the shielding properties).
|